Accelerated pitting corrosion test of 304 stainless steel using ASTM G48; Experimental investigation and concomitant challenges

Bhandari, J, Lau, S, Abbassi, R ORCID: 0000-0002-9230-6175, Garaniya, V ORCID: 0000-0002-0090-147X, Ojeda, R ORCID: 0000-0002-2421-0032, Lisson, D and Khan, FI ORCID: 0000-0002-5638-4299 2017 , 'Accelerated pitting corrosion test of 304 stainless steel using ASTM G48; Experimental investigation and concomitant challenges' , Journal of Loss Prevention in The Process Industries, vol. 47 , pp. 10-21 , doi: 10.1016/j.jlp.2017.02.025.

Full text not available from this repository.

Abstract

Marine and offshore structures constructed with stainless steel are regarded as having high corrosion resistance due to their superior self-passivating properties. However, they are equally susceptible to environmental degradation, especially due to pitting corrosion in highly corrosive marine environments. Pitting immersion tests performed on 304 austenitic stainless steel specimens using ASTM G48 presented significant challenges. Some of the issues encountered during these tests included unspecified experimental factors that control the pitting process such as pH, specimen size limitations, materials’ properties, and the variation on the quality of the test solution. To overcome these challenges, the effect of surface finishes and aeration of the test solution on the corrosion behavior of 304 stainless steel specimens in 6% ferric chloride were examined and compared. The result shows that an aerated solution has much lower concentrations of pits compared to quiescent solutions. Controlled aeration eliminates unwanted crevice corrosion background noise. Subsequently, to suit larger specimens, the ASTM G48 was modified. This study presents the modified ASTM G48 procedure. A series of pitting corrosion tests on stainless steel specimen with different thickness were conducted and data were statistically evaluated. The generalized extreme value distribution, such as Weibull, provides adequate statistical descriptions of the pit depth and pit diameter distributions. The modified ASTM G48 offered advantages in the extraction and interpretation of the data for pit characteristics in the accelerated pitting corrosion test simulating actual marine environment.

Item Type: Article
Authors/Creators:Bhandari, J and Lau, S and Abbassi, R and Garaniya, V and Ojeda, R and Lisson, D and Khan, FI
Keywords: corrosion, offshore structures, ASTM G48, experiment, pitting, large specimens, stainless steel, Weibull distributions
Journal or Publication Title: Journal of Loss Prevention in The Process Industries
Publisher: Elsevier Ltd
ISSN: 0950-4230
DOI / ID Number: 10.1016/j.jlp.2017.02.025
Copyright Information:

© 2017 Elsevier

Related URLs:
Item Statistics: View statistics for this item

Actions (login required)

Item Control Page Item Control Page
TOP